Titanium dioxide anatase and rutile
Titanium dioxide anatase
TiO2 content >=98.5%
Whiteness no less than the standard GB1706-93
scattering no less than the standard GB1706-93
volitilation at 105degree <=0.5%
PH value when suspensted on water 6.8-7.3
Oil Absorption <=25g/100g
Sieve Residue(0.045mm) <=0.05%
Water extraction electrical resistance >=30
water absorption value <=28g/100g
water dispesible power >=80
Titanium dioxide rutile
Inorganic suface treatment Al2O3,ZrO2
Organic surface treatment yes
TiO2 content >=93%
Brightness >=98%
Tint reducing powder,reynolds unmber,TCS >=1850
Volitilation at 105degree <=0.6%
Water solublition <=0.5%
PH value when suspensted on water 6.5-8.5
Oil Absorption <=20g/100g
Electrical resistance of water extraction >=80
Sieve Residue(0.045mm) <=0.0.2%
Rutile content >=98%